IEC 60793-1-32:2018 光纤 - 第1-32部分:测量方法和测试程序 - 涂层剥离性

标准编号：IEC 60793-1-32:2018

中文名称：光纤 - 第1-32部分:测量方法和测试程序 - 涂层剥离性

英文名称：Optical fibres - Part 1-32: Measurement methods and test procedures - Coating strippability

发布日期：2018-11-16

标准范围

IEC 60793-1-32:2018作为IEC 60793-1-32:2018 RLV提供，其中包含国际标准及其红线版本，显示了与上一版本相比技术内容的所有变化。IEC 60793-1-32:2018主要用于测试纤维制造商生产的纤维或随后使用各种聚合物进行外涂层（紧密缓冲）的纤维。测试可以在生产的纤维上进行，或者在暴露于各种环境之后进行。本试验适用于标称玻璃尺寸为125 μ m的A1、A2、A3、B和C纤维。本文件的目的是建立机械特性-涂层剥离性的统一要求。该测试量化沿其纵轴从光纤机械移除保护涂层所需的力。该测试不是为了在去除涂层后使光纤强度最大化，也不是为了指定光纤现场剥离的最佳条件。本试验设计用于标称外径在200 μ m至900 μ m范围内的聚合物涂层的光纤。？这第三版取消并取代了2010年出版的第二版。本版构成技术修订版。该版本相对于上一版本包括以下重大技术变化:扩大了适用于本文详述的方法的涂层尺寸范围，以适应具有200 μ m涂层尺寸的光纤。关键词:涂层剥离性，光纤保护涂层

IEC 60793-1-32:2018 is available as IEC 60793-1-32:2018 RLV which contains the International Standard and its Redline version, showing all changes of the technical content compared to the previous edition.

IEC 60793-1-32:2018 is intended primarily for testing either fibres as produced by a fibre manufacturer or subsequently overcoated (tight buffered) using various polymers. The test can be performed either on fibres as produced, or after exposure to various environments. This test applies to A1, A2, A3, B and C fibres with a nominal glass dimension of 125 μm. The object of this document is to establish uniform requirements for the mechanical characteristic – coating strippability. This test quantifies the force required to mechanically remove the protective coating from optical fibres along their longitudinal axis. This test is not intended as a means to maximize fibre strength after the coating is removed nor is it intended to specify the best conditions for field stripping of optical fibres. This test is designed for optical fibres having polymeric coatings with nominal outer diameters in the range of 200 μm to 900 μm.？ This third edition cancels and replaces the second edition published in 2010. This edition constitutes a technical revision. This edition includes the following significant technical change with respect to the previous edition: expansion of the range of coating dimensions applicable to the procedure detailed in this document to accommodate optical fibres with a 200 μm coating dimension.

Keywords: coating strippability, protective coating of optical fibres